Laticonther 57 CPG/550
| Category: | PPA , Polyphthalamide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laticonther |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qLXLBe_Laticonther-57-CPG-550.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High thermal conductivity product based on Semi-aromatic polyammide (PPA). Special filler. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.99 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.65 | % | |
| Flow : 2.00 mm | 0.30 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.60 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Thermal Conductivity | 1.2 | W/m/K | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 310 to 330 | °C | |
| Mold Temperature | 140 to 160 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 126F5 | SAX Polymers | Nylon 6 | SAXAMID™ |
| Teflon® PTFE CFP 6000 X | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| NaturePlast NP DU 203 | NaturePlast | Nylon 1012 | NaturePlast |
| ESTOPLAST ZK 8505GY46 | Ester Industries Ltd. | PC+ABS | ESTOPLAST ZK |
| Kepital® F20-33 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |