API PS 392
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | American Polymers, Inc. |
| Trademark: | API PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qIuRmZ_API-PS-392.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
API 392 is a general purpose polystyrene produced in pellet form for injection molding. API 392 has excellent clarity and high flow. Application: Used in the manufacture of containers, housewares, toys, and medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 71 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ASTM D638 |
| Tensile Strength (Break) | 42.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 87.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.8 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 177 to 232 | °C | |
| Front Temperature | 191 to 274 | °C | |
| Mold Temperature | -6.67 to 71.1 | °C | |
| Injection Pressure | 34.5 to 276 | MPa | |
| Back Pressure | 0.0689 to 3.45 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 12.NA | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| Resinoid 2002-4P | Resinoid Engineering Corporation | Phenolic | Resinoid |
| TECHNYL® A 60G1 V25 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Fainplast PVC PM 8010/S | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| HiFill® PBT FR-DE | Techmer Engineered Solutions | PBT | HiFill® |