Hifax TRC 1204P
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qHnMBV_Hifax-TRC-1204P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hifax TRC 1204P has a very high melt flow, very high flexural modulus, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of properties and processability. It was designed for use in multiple automotive exterior applications and for applications requiring high stiffness and low CLTE. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 17.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Multi-Axial Instrumented Impact Energy 1(-10°C, Energy to Peak Force, Ductile Failure) | 21.0 | J |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE | |||
| Flow | 2.7E-5 | cm/cm/°C | |
| Transverse | 2.7E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 2.2 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® NBR DN1001 | Zeon Corporation | NBR | Nipol® NBR |
| Badaflex® TPE-S 60A 1344 LD GR | Bada AG | SEBS | Badaflex® |
| Akulon® XP36-E1 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Chemlon® 412 H | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Karina BLACK PVC COMPOUND 70900-48/1-F-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |