PRL TP-GP1
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qHXCLz_PRL-TP-GP1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL TP-GP1 is a Polybutylene Terephthalate (PBT) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 12 to 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.6 to 2.2 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.080 | % | |
| Equilibrium, 23°C | 0.34 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 117 | ASTM D785 | |
| M-Scale | 78 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 51.7 | MPa | |
| Break, 3.18 mm | 51.7 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 3.5 | % | |
| Break, 3.18 mm | 200 | % | |
| Flexural Modulus (3.18 mm) | 2310 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.3 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 53 | J/m | ASTM D256 |
| 23°C | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C, 3.18 mm) | 1600 | J/m | ASTM D4812 |
| Gardner Impact (3.18 mm) | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 149 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 52.8 | °C | |
| Vicat Softening Temperature | 190 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.59 mm, in Oil | 23 | kV/mm | |
| 3.18 mm, in Air | 15 | kV/mm | |
| 3.18 mm, in Oil | 15 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.30 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 232 to 249 | °C | |
| Middle Temperature | 238 to 254 | °C | |
| Front Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 43.3 to 76.7 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA ABS 4135 | MBA Polymers | ABS | MBA ABS |
| Nymax™ 1010 A HS Black 13 | PolyOne Corporation | Nylon 6 | Nymax™ |
| ALAMID® 6.6 CF 40 SCHWARZ-9908 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
| DJSilicone NE-631 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Rotec® ABS 2001 TR-AC | ROMIRA GmbH | ABS | Rotec® ABS |