Leona™ 90G33
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qHUDYq_Leona-90G33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ 90G33 is a Polyamide 66 (Nylon 66) product filled with 33% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 90G33 include automotive, engineering/industrial parts and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.39 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.4 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.4 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 90 | -- | ||
| R-Scale | 120 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10200 | 9300 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 180 | 150 | MPa | ISO 527-2 |
| -- | 194 | 157 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 3.0 | 4.0 | % | ASTM D638 |
| Break, 23°C | 2.5 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 9600 | 7600 | MPa | ASTM D790 |
| 23°C | 10000 | 8100 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 294 | 245 | MPa | ASTM D790 |
| 23°C | 238 | 216 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 55 | 54 | kJ/m² | ISO 179 |
| Notched Izod Impact | 98 | 120 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 235 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | -- | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ WS-53NF | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| TRIREX® Compound 3025PG20 | Samyang Corporation | PC | TRIREX® Compound |
| Kumho ABS 775EG | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| Hostacom D1172 9177 | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| LIHAN® S9000EP | Nanjing Lihan Chemical Co., Ltd. | ABS | LIHAN® |