NORYL™ BN9003G resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qH5BXd_NORYL-BN9003G-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PS blend. Unfilled. Blow molding. Excellent balance of impact and surface aesthetics. Suitable for automotive exterior components including spoilers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.55 - 0.75 | % | Internal method |
| Flow : 3.20mm | 0.55 - 0.75 | % | Internal method |
| Transverse flow : 3.20mm | 0.55 - 0.75 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.25 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2240 | MPa | ASTM D638 |
| -- | 2170 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 48.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 42.0 | MPa | ASTM D638 |
| Fracture | 42.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 3.6 | % | ASTM D638 |
| Yield | 3.4 | % | ISO 527-2/50 |
| Fracture 6 | 45 | % | ASTM D638 |
| Fracture | 30 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 7 | 2150 | MPa | ASTM D790 |
| -- 8 | 2190 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 75.0 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | ISO 179/1eA |
| 23°C | 26 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 11 | ISO 179/1eU | ||
| -30°C | 110 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 130 | J/m | ASTM D256 |
| 23°C | 320 | J/m | ASTM D256 |
| -30°C 12 | 10 | kJ/m² | ISO 180/1A |
| 23°C 13 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812, ISO 180/1U | |
| -30°C 14 | 54 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 40.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 124 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 15 | 126 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 108 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 16 | 110 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ASTM D1525 17 |
| -- | 127 | °C | ISO 306/B50 |
| -- | 130 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.0 - 87.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 226 - 258 | °C | |
| Cylinder Zone 2 Temp. | 231 - 258 | °C | |
| Cylinder Zone 3 Temp. | 237 - 258 | °C | |
| Cylinder Zone 4 Temp. | 237 - 258 | °C | |
| Cylinder Zone 5 Temp. | 237 - 258 | °C | |
| Adapter Temperature | 237 - 258 | °C | |
| Die Temperature | 237 - 258 | °C |
| Extrusion instructions |
|---|
| Head - Zone 6 - Top Temperature: 237 - 258 °CHead - Zone 7 - Bottom Temperature: 237 - 258 °CHead - Zone 7 - Middle Temperature: 237 - 258 °CMelt Temperature (Parison): 237 - 258 °CMold Temperature: 66 - 93 °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 mm |
| 16 . | 80*10*4 mm |
| 17 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V80B | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| Prixene® EL020E20 | POLYMAT | LLDPE | Prixene® |
| Vydyne® 22HSP | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| BMC T60-6006 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| POTICON OA10 | Otsuka Chemical Co., Ltd. | Acetal (POM) Copolymer | POTICON |