OPNYL OP6GF15
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | OPNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qGg5m8_OPNYL-OP6GF15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 6 - Glass reinforced (15 %), high tensile strength, stiffness and HDT. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.25 | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.20 | 0.10 to 0.20 | % | ASTM D955 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1 | 4800 | 3100 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 145 | 85.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | 4.0 | % | ASTM D638 |
| Flexural Modulus 4 | 5000 | 3400 | MPa | ASTM D790 |
| Flexural Strength 5(Yield) | 150 | 115 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | 85 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed, 3.20 mm | 208 | -- | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 200 | -- | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PA6 C 2010/506 GF10 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Geon™ HC 2180 | PolyOne Corporation | PVC, Flexible | Geon™ HC |
| LITEN BB 75 | UNIPETROL RPA | HMWPE | LITEN |
| ESTOPLAST XU 43251GY01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |
| LNP™ LUBRICOMP™ OCP36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |