Crastin® LW9320 BK851
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qGYfQi_Crastin-LW9320-BK851.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 6.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 165 | °C | ISO 75-2/A |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 32 | mm/min | ISO 3795 |
| Flammability Classification (0.750 mm) | HB | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2522C | Teknor Apex Company | TPE | Telcar® |
| Witcobond® W-242 | Chemtura | PUR-Ester | Witcobond® |
| Anjacom® 200C-P | Almaak International GmbH | Nylon 6 | Anjacom® |
| Karina BROWN COLOR CONCENTRATE 36/ 19-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polygen SG8A | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |