Nymax™ GF 924 33 UV Black 108
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Nymax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qGGbqf_Nymax-GF-924-33-UV-Black-108.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nymax™GF 924 33 UV Black 108 is a polyamide 66 (nylon 66) product, which contains a filler of 33% glass fiber reinforcement. It can be processed by injection molding and is available in North America or Latin America. Nymax™The application fields of GF 924 33 UV Black 108 include industrial application, construction application, automobile industry and consumer goods. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.39 | g/cm³ | ASTM D792 |
| -- | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr | 1.0 | % | ASTM D570 |
| 23°C, 24 hr | 0.90 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 8780 | MPa | ISO 178 |
| -- | 1820 | MPa | ISO 527 |
| -- | 8620 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 1 | 169 | MPa | ASTM D638 |
| Fracture | 136 | MPa | ISO 527 |
| Tensile Elongation | |||
| Yield 2 | 3.0 | % | ASTM D638 |
| Fracture | 8.8 | % | ISO 527 |
| Flexural Modulus | 8620 | MPa | ASTM D790 |
| Flexural Strength | |||
| -- | 207 | MPa | ISO 178 |
| -- | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 91 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, annealed, 3.18mm | 221 | °C | ASTM D648 |
| 1.8 MPa, annealed | 227 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Molded Test Bars: Dry as Molded |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 82.2 - 107 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 271 - 293 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® F34 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Quadrant EPP CESTILENE HD 500 | Quadrant Engineering Plastic Products | HMWPE | Quadrant EPP |
| TEKNIFLEX® VA1090 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
| Capilene® U 77 A | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| EVICOM™ RG7/915 | INEOS Compounds | PVC, Rigid | EVICOM™ |