Ultramid® T 4381 LDS SW23271
| Category: | Nylon 6/6T , Polyamide 6/6T Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qFhYyx_Ultramid-T-4381-LDS-SW23271.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass fibre and mineral reinforced partially aromatic polyamide for injection moulding. Good toughness, stiffness and strength, low water absorption, high melting point (295 °C). The product is especially tailored for laser direct structuring (LDS). The structured areas can be metallized selectively. The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser & Electronics AG (Osteriede 7 - 30827 Garbsen - Germany). The use of this process asserts a claim for compensation. After purchasing a LPKF laser system the claim is satisfied. Please contact directly LPKF Laser & Electronics AG (http://www.LPKF.de). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.60 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.2 to 5.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.80 to 1.2 | -- | % | |
| Viscosity Number (96% H2SO4 (Sulphuric Acid)) | 130 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 110 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | -- | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 35 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 265 | -- | °C | ISO 75-2/B |
| Melting Temperature | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 80°C | 3.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 80°C | 5.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 4.40 | 4.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | 0.038 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 310 to 330 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPB200 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| AvaSpire® AV-722 CF30 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| Europrene® N 2860 GRN | Versalis S.p.A. | NBR | Europrene® |
| ENVIROLOY® ENV15-NC710 | ENVIROPLAS®, Inc. | PC+ABS | ENVIROLOY® |
| TOTAL Polyethylene Lumicene® M 3583 UV black | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |