CYCOLAC™ FR23 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qFTsDd_CYCOLACFR23resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame retardant ABS (non-PBBE additives). Good properties/toughness. Excellent moldability. UL94 V-0 rated. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 6.8 | g/10 min | ASTM D1238 |
| 220°C/5.0 kg | 9.8 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 37.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2410 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 42.7 | MPa | ASTM D638 |
| Fracture | 35.2 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 2.1 | % | ASTM D638 |
| Fracture | 11 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2720 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 73.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 270 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 41.8 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 83.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 72.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.31 mm | V-0 | UL 94 | |
| 2.49 mm | 5VB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (200°C, 1000 sec^-1) | 310 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Rear Temperature | 171 - 182 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 199 - 216 | °C | |
| Nozzle Temperature | 199 - 221 | °C | |
| Processing (Melt) Temp | 199 - 221 | °C | |
| Mold Temperature | 48.9 - 71.1 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 0299 X 119106 H | RTP Company | Nylon 66 | RTP |
| Siloxane Masterbatch MB50-010 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| TEKAMID™ TA250GM | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Formolon® 622 | Formosa Plastics Corporation, U.S.A. | PVC, Rigid | Formolon® |
| PEARLCOAT® Activa D118K | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLCOAT® |