TRIEL® HV5401BH
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | Samyang Corporation |
| Trademark: | TRIEL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qEo4TP_TRIEL-HV5401BH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIEL® HV5401BH is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in Asia Pacific, Europe, or North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 1.7 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Break | 23.5 | MPa | |
| 5.0% Strain | 5.88 | MPa | |
| 10% Strain | 8.34 | MPa | |
| 50% Strain | 12.7 | MPa | |
| Tensile Elongation (Break) | > 400 | % | ASTM D638 |
| Flexural Modulus | 90.2 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 5.88 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 160 | °C | ASTM D1525 1 |
| Melting Temperature | 205 | °C | ASTM D2117 |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mecoline S RDX 1203 F | Melos GmbH | TP, Unspecified | Mecoline |
| Stylac™ 191F | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| SynPlast™ DIDA-E | PolyOne Corporation | Di Isodecyl Adipate | SynPlast™ |
| MTM® 56 series | Cytec Industries Inc. | Epoxy | MTM® |
| ACCUTECH™ HD0234G10UVL | ACLO Compounders Inc. | HDPE | ACCUTECH™ |