Smooth-On EA-40®
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Smooth-On |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qEfoqV_Smooth-On-EA-40-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EA-40® Clear Epoxy is an unfilled low-viscosity epoxy adhesive that can be spread easily in thin films that are almost transparent after curing. EA-40® has a long pot life and cures in 24 hours at room temperature to provide good mechanical and electrical properties. Mix ratio is 1:1 by volume. When mixed 2A:1B by volume, EA-40® will achieve greater heat resistance and improved physical properties. EA-40® is versatile and can be used for many different assembly and repair applications ranging from electrical potting to jewelry assembly to repairing plumbing fixtures. Bow makers have come to know EA-40® as a tremendous laminating resin. EA-40® provides highly moisture resistant bonds meeting the performance requirements for Federal Specification MMM-A-188, Type III. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Viscosity | Light-paste |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Mixing Ratio | 1A:1B by volume or weight | ||
| Sag Resistance | 1.59 | mm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 66 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1310 | MPa | ASTM D638 |
| Tensile Strength | 23.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Compressive Modulus | 965 | MPa | ASTM D695 |
| Compressive Strength | 55.8 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life (23°C) | 120 | min | |
| Demold Time | 1400 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILSAN A GP | Taro Plast S.p.A. | ASA | NILSAN |
| Huaxia Shenzhou PFA DS708-B | Shandong Huaxia Shenzhou New Material Co., Ltd. | PFA | Huaxia Shenzhou |
| LG PVC LS300 | LG Chem Ltd. | PVC Homopolymer | LG PVC |
| Karina YELLOW PVC COMPOUND -E 701D02/128-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Daelim Po1y® XP3200 | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |