Chemlon® E-66 GF30 Datasheet,Nylon 66,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
Chemlon® E-66 GF30 is an economy range 30% glass fibre reinforced Nylon 66 compound. It is available in natural or black versions.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Appearance	Black Natural color
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.37	g/cm³	ISO 1183
Molding Shrinkage ¹	0.30 - 0.70	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	1.8	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	8000	MPa	ISO 527-2
Tensile Stress (Break)	165	MPa	ISO 527-2
Tensile Strain (Break)	3.0	%	ISO 527-2
Flexural Modulus	7000	MPa	ISO 178
Flexural Stress ²	195	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	7.0	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 240	°C	ISO 75-2/B
1.8 MPa, not annealed	230	°C	ISO 75-2/A

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Rear Temperature	275 - 300	°C
Middle Temperature	275 - 300	°C
Front Temperature	275 - 300	°C
Processing (Melt) Temp	< 300	°C
Mold Temperature	80.0 - 90.0	°C
Injection Rate	Fast
Screw Speed	50 - 200	rpm

Injection instructions
Back pressure: LowInjection pressure: HighThe material is supplied dry and ready to mould in sealed, moisture proof sacks. No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. Should drying become necessary, two hours at 80°C in a dehumidifying drier is recommended. The use of air circulating driers is not generally recommended, as longer drying times are often required, with greater potential for product oxidation and yellowing. Drying temperatures should not exceed 80°C.

Injection instructions

Back pressure: LowInjection pressure: HighThe material is supplied dry and ready to mould in sealed, moisture proof sacks. No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. Should drying become necessary, two hours at 80°C in a dehumidifying drier is recommended. The use of air circulating driers is not generally recommended, as longer drying times are often required, with greater potential for product oxidation and yellowing. Drying temperatures should not exceed 80°C.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).
2 .	At Break

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

2 .

At Break

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	qERND8_Chemlon-E-66-GF30.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Shandong PP PF01	Shandong Dongchen Engineering Plastics Co., Ltd.	PP, Unspecified	Shandong PP
VITAMIDE® AR3XBK8510	Jackdaw Polymers	Nylon 66	VITAMIDE®
TPUCO® TPU-C85	Taiwan PU Corporation	TPU-Polyester	TPUCO®
Karina BLACK PVC COMPOUND 850D48/ 1-D-IS-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
RTP 199 X 136882 B	RTP Company	PP, Unspecified	RTP