LubriOne™ ES-10CF/15T BLACK
| Category: | PESU , Polyethersulfone |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qE2LwC_LubriOne-ES-10CF-15T-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE lubricated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 5170 | MPa | ASTM D638 |
| Tensile Strength 2 | 103 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 4 | 7500 | MPa | ASTM D790 |
| Flexural Strength 5 | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 204 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 160 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 340 - 380 | °C | |
| Middle Temperature | 340 - 380 | °C | |
| Front Temperature | 340 - 380 | °C | |
| Mold Temperature | 140 - 160 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ferro PP JPP60BX03NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| DuraGrip® DGR 6165TR | Advanced Polymer Alloys | TPE | DuraGrip® |
| Hylon® N2230HL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| 3M™ Dyneon™ PTFE Compound FC 15025 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Durethan® B 40 FAM 000000 | LANXESS Corporation | Nylon 6 | Durethan® |