Petrothene® NA940085
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qDF6vq_Petrothene-NA940085.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA940 is a series of resins used for heavy duty film applications. Excellent puncture resistance combined with impact properties make NA940 an exceptional choice when selected by customers for bags used to package fertilizer, peat moss, decorative stone and agricultural and construction materials. NA940 also has excellent heat shrink properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, F0) | 168 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 14.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 600 | % | ASTM D638 |
| Flexural Modulus | 234 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm | 165 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm | 186 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 20.7 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 19.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 300 | % | ASTM D882 |
| TD : Fracture, 51 µm | 500 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 220 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 220 | g | ASTM D1922 |
| TD : 51 µm | 200 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 166 - 221 | °C |
| Extrusion instructions |
|---|
| NA 940 has been designed for excellent processability, bubble stability and good heat sealing over a wide range of extrusion conditions. Optimum properties are found at melt temperatures of 330°-430°F (165°-221°C) and blow-up ratios between 1.8:1 and 2.5:1. Drawdown to 1.5 mil (38.1 microns) is possible at commercial rates when proper extrusion techniques are used. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-255 | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| THERMOLAST® K TC7FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Geon™ Vinyl Rigid Extrusion L7007 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| OmniCarb™ PC/ABS 1228 | OMNI Plastics, LLC | PC+ABS | OmniCarb™ |
| TechnoFiber Performance PP LGF 30-10-02 HI | TechnoCompound GmbH | PP, Unspecified | TechnoFiber Performance |