AURAMID PAGF50 BK
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Aurora Manufacturing Ltd |
| Trademark: | AURAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qD8zfG_AURAMID-PAGF50-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PAGF30 BK is a general purpose 50% glass filled black PA compound manufactured from recycled polymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 155 | MPa | ISO 527-2 |
| Tensile Strain (Break) | < 5.0 | % | ISO 527-2 |
| Flexural Modulus | > 7500 | MPa | ISO 178 |
| Flexural Stress | > 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | > 5.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | > 225 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 255 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 235 to 285 | °C | |
| Middle Temperature | 235 to 285 | °C | |
| Front Temperature | 235 to 285 | °C | |
| Mold Temperature | 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Homopolymer PP700 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| ALAMID® 6 GF 30 PU D SCHWARZ-17018 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | ALAMID® |
| GELOY™ FXW710SK resin | SABIC Innovative Plastics | ASA | GELOY™ |
| elitel UE3240 | UNITIKA Plastics Division | TPC-ET | elitel |
| Sylvin 9302-70 FUV WHITE 1337 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |