FOZEAS® J9501E50
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | FOZEAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qD5NE5_FOZEAS-J9501E50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FOZEAS® J9501E50 is a Polylactic Acid (PLA) material. It is available in Asia Pacific for extrusion. Important attributes of FOZEAS® J9501E50 are:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.26 | g/cm³ | JIS K7112 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.20 | g/10 min | JIS K7210 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 50.0 | MPa | JIS K7161 |
| Tensile Strain (Break) | 140 | % | JIS K7161 |
| Flexural Modulus | 3000 | MPa | JIS K7171 |
| Flexural Stress | 75.0 | MPa | JIS K7171 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact Strength | 10 | kJ/m² | JIS K7110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | JIS K7191-1 |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 2550®B-AM-CR-SX | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| TAROMID B 280 Z2 G6 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| OXPEKK® IG100 | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |
| PENTAMID B GV10 GK20 H LS black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| LNP™ VERTON™ NV008E compound | SABIC Innovative Plastics | PC+ABS | LNP™ VERTON™ |