POCAN® B 7616 000000
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | LANXESS Corporation |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qD3gwg_POCAN-B-7616-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT+PC, 15 % glass fibers, injection molding, low tendency to warp, improved surface finish |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.35 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 250°C, 2.00 mm 1 | 0.50 | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.20 | % | |
| Flow : 250°C, 2.00 mm 3 | 0.70 | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.40 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 160 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 75.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.2 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 4500 | MPa | ISO 178/A |
| Flexural Stress 6 | |||
| 3.5% Strain | 120 | MPa | ISO 178/A |
| 23°C | 130 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 4.7 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT+PC, GHMR, 09-050, GF15 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 35 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 75.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 145 | °C | ISO 306/B120 |
| Ball Pressure Test (150°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 8.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 5.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 34 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.50 | ||
| 23°C, 1 MHz | 3.40 | ||
| Dissipation Factor (23°C, 1 MHz) | 0.013 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 250 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; WZ 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; WZ 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPC PVC SG730 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Aplax P1017GB | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| KRALASTIC® SR | Nippon A&L Inc. | ABS | KRALASTIC® |
| IDI BMC Rosite 3550C | IDI Composites International | TS, Unspecified | IDI BMC |
| POLYelast TPE ED80 D40 UV | Polykemi AB | PP+EPDM | POLYelast |