Generic PC+PBT
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qCWBsM_Generic-PC-PBT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC+PBT This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 - 1.24 | g/cm³ | ASTM D792 |
| 23°C | 1.17 - 1.34 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 - 0.80 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 8.7 - 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 7.00 - 13.3 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.29 - 1.3 | % | ASTM D955 |
| Transverse flow : 23°C | 0.60 - 1.7 | % | ASTM D955 |
| 23°C | 0.79 - 1.5 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.042 - 0.21 | % | ASTM D570 |
| 23°C, 24 hr | 0.080 - 0.50 | % | ISO 62 |
| Saturated, 23°C | 0.071 - 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.046 - 0.21 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 89 - 117 | ASTM D785 | |
| Ball Indentation Hardness | 81.8 - 108 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1810 - 2250 | MPa | ASTM D638 |
| 23°C | 1880 - 2220 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 43.5 - 66.4 | MPa | ASTM D638 |
| Yield, 23°C | 44.0 - 60.5 | MPa | ISO 527-2 |
| Fracture, 23°C | 40.3 - 61.2 | MPa | ASTM D638 |
| Fracture, 23°C | 39.6 - 60.6 | MPa | ISO 527-2 |
| 23°C | 47.7 - 60.5 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 3.7 - 7.6 | % | ASTM D638 |
| Yield, 23°C | 3.3 - 5.1 | % | ISO 527-2 |
| Fracture, 23°C | 1.5 - 150 | % | ASTM D638 |
| Fracture, 23°C | 18 - 150 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 10 - 51 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1450 - 2430 | MPa | ASTM D790 |
| 23°C | 1880 - 2510 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 66.9 - 91.4 | MPa | ASTM D790 |
| 23°C | 64.3 - 95.0 | MPa | ISO 178 |
| Yield, 23°C | 66.7 - 102 | MPa | ASTM D790 |
| Fracture, 23°C | 69.0 - 83.3 | MPa | ASTM D790 |
| Taber Abrasion Resistance (23°C) | 30.0 - 30.6 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 - 61 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 38 - 820 | J/m | ASTM D256 |
| 23°C | 30 - 65 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 48.6 - 71.1 | J | ASTM D3763 |
| 23°C | 45.0 - 110 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 87.5 - 245 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 90.0 - 125 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 72.8 - 107 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 73.6 - 90.5 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 117 - 136 | °C | ASTM D1525 |
| -- | 114 - 136 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 225 | °C | ISO 11357-3 |
| -- | 225 - 226 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | |||
| Flow | 1.5E-5 - 6.5E-5 | cm/cm/°C | ASTM D696 |
| Flow | 7.9E-5 - 9.1E-5 | cm/cm/°C | ASTM E831 |
| Flow | 8.1E-5 - 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.5E-5 - 1.1E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 9.0E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.18 - 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 74.0 - 130 | °C | UL 746 |
| RTI Imp | 74.0 - 130 | °C | UL 746 |
| RTI | 74.0 - 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.5E+10 - 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+13 - 1.0E+18 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+14 - 2.5E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 18 - 25 | kV/mm | ASTM D149 |
| 23°C | 17 - 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.00 - 3.20 | ASTM D150 | |
| 23°C | 3.19 | IEC 60250 | |
| Dissipation Factor (23°C) | 1.9E-3 - 0.020 | IEC 60250 | |
| Arc Resistance | 82.5 - 131 | sec | ASTM D495 |
| Comparative Tracking Index | 113 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 720 - 828 | °C | IEC 60695-2-13 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 210 - 261 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 94.0 - 123 | °C | |
| Drying Time | 2.8 - 5.2 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Max Moisture | 0.020 - 0.024 | % | |
| Suggested Shot Size | 60 - 65 | % | |
| Hopper Temperature | 50.0 - 50.5 | °C | |
| Rear Temperature | 239 - 259 | °C | |
| Middle Temperature | 252 - 261 | °C | |
| Front Temperature | 251 - 267 | °C | |
| Nozzle Temperature | 251 - 265 | °C | |
| Processing (Melt) Temp | 250 - 271 | °C | |
| Mold Temperature | 61.5 - 76.9 | °C | |
| Back Pressure | 0.172 - 0.534 | MPa | |
| Screw Speed | 43 - 76 | rpm | |
| Vent Depth | 0.017 - 0.033 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC+PBTThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Primefin V500TL40 | Lucent Polymers, Inc. | PP Homopolymer | Primefin |
| API PS 410 | American Polymers, Inc. | PS (GPPS) | API PS |
| Durolon® IR2000 CR010 | Unigel Plásticos | PC | Durolon® |
| HiFill® PP GF/M50 BK | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| LNP™ THERMOCOMP™ RF00CSXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |