Daicel PP PT8F1
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Daicel PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qBufsr_Daicel-PP-PT8F1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Daicel PP PT8F1 is a Polypropylene material filled with 40% talc. It is available in Asia Pacific. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.80 to 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 86 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2 |
| Flexural Modulus | 4300 | MPa | ISO 178 |
| Flexural Stress | 42.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 135 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 140 to 190 | °C | |
| Middle Temperature | 160 to 210 | °C | |
| Front Temperature | 180 to 230 | °C | |
| Nozzle Temperature | 180 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 5.00 to 20.0 | MPa | |
| Screw Speed | 70 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BMC T60-6006 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Carbo-Rite™ B-260 | Lubrizol Advanced Materials, Inc. | PP, Unspecified | Carbo-Rite™ |
| Electroblend® PP-1900 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Homopolymer | Electroblend® |
| Karina GREEN PVC COMPOUND -E810-40/312-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PERLER® N09H2500B11 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |