Asrene® SP 4808
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chandra Asri Petrochemical |
| Trademark: | Asrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qBKVP3_Asrene-SP-4808.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Asrene® SP 4808 is a High Density Polyethylene product. It can be processed by extrusion and is available in Asia Pacific, Europe, or North America. Typical application: Plumbing/Piping/Potable Water. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.060 | g/10 min | |
| 190°C/21.6 kg | 9.0 | g/10 min | |
| 190°C/5.0 kg | 0.25 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal, F50) | > 1000 | hr | ASTM D1693 |
| Viscosity (190°C) 1 | > 100000000 | mPa·s |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Slow Crack Growth Resistance - Notch Test (80°C) 2 | > 1058 | hr |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 80 | min | ASTM D3895 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hydrostatic Resistance 3 | ISO 1167 | ||
| 12.4 MPa : 20°C | > 4.2 | day | |
| 5.0 MPa : 80°C | > 41.7 | day | |
| 5.5 MPa : 80°C | > 6.9 | day | |
| Longitudinal Reversion 4 | 0.63 | % | ISO 2505-1, -2 |
| Rapid Crack Propagation - S4 Test (0°C) 5 | > 1.20 | MPa | ISO 13477 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 30.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Elongation (Break) | > 700 | % | ASTM D638 |
| Flexural Modulus | 1300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 550 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 0.1 sec^-1, Torque Rheometer |
| 2 . | 9.2 bar, PE-100, S-5, SDR-11, PN-16, OD-110mm |
| 3 . | PE-100, S-5, SDR-11, PN-16, OD-32mm |
| 4 . | PE-100, S-5, SDR-11, PN-16, OD-110mm |
| 5 . | PE-100, S-5, SDR-11, PN-16, OD-110mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6926 NA 021 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Razalen® Q111 | Razin™ Engineering Plastics | PP Homopolymer | Razalen® |
| UNISOFT TPE™ ST-45A-BK-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Aaroprene® ATPO 3000 70A | Aaron Industries Corp. | TPO (POE) | Aaroprene® |
| K-Resin® SBC KR01 | Chevron Phillips Chemical Company LLC | SBC | K-Resin® SBC |