LNP™ THERMOCOMP™ MFB41I compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qB8tUV_LNPTHERMOCOMPMFB41Icompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Thermocomp* MFB41I is a compound based on Polypropylene resin containing Glass Fiber, Glass Bead. Added features include: Chemically Coupled Also known as: LNP* THERMOCOMP* Compound MFB41I Product reorder name: MFB41I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.60 - 0.80 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2450 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.1 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 2300 | MPa | ISO 178 |
| Flexural Stress | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 134 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 82.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.4E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 216 - 227 | °C | |
| Front Temperature | 238 - 249 | °C | |
| Processing (Melt) Temp | 227 - 249 | °C | |
| Mold Temperature | 32 - 49 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP TIVAR® 1000 EC | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| SLOVASTER® B1 GF 10 FRX 5 | Plastcom | PBT | SLOVASTER® |
| Moplen HP300R | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| TRANSMARE® 14CT20-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Colorite 77 Series 8577 | Colorite Polymers | PVC, Unspecified | Colorite 77 Series |