Tritan™ MX710
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tritan™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qB5eCR_Tritan-MX710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastman Tritan™ Copolyester MX710 is an amorphous product with excellent appearance and clarity. Eastman Tritan™ Copolyester MX710 has many outstanding features that include excellent toughness, hydrolytic stability, heat resistance, and chemical resistance. Eastman Tritan™ Copolyester MX710 has been formulated for medical devices. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1550 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 43.0 | MPa | ASTM D638, ISO 527-2 |
| Break, 23°C | 53.0 | MPa | ASTM D638 |
| Break, 23°C | 58.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 6.0 | % | ASTM D638 |
| Yield, 23°C | 7.0 | % | ISO 527-2 |
| Break, 23°C | 210 | % | ASTM D638 |
| Break, 23°C | 190 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1550 | MPa | ASTM D790 |
| 23°C | 1500 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 59.0 | MPa | ISO 178 |
| Yield, 23°C | 62.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 110 | J/m | ASTM D256 |
| 23°C | 980 | J/m | ASTM D256 |
| -40°C | 20 | kJ/m² | ISO 180 |
| 23°C | 93 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D4812 | ||
| -40°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Energy at Peak Load | 66.0 | J | |
| 23°C, Energy at Peak Load | 61.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 99.0 | °C | |
| 1.8 MPa, Unannealed | 85.0 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total) | 90.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 282 | °C | |
| Mold Temperature | 38.0 to 66.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVALAC RX®448 | Vyncolit N.V. | Phenolic | NOVALAC |
| ADDINYL C2 ZV20 | ADDIPLAST | Nylon 66/6 | ADDINYL |
| LNP™ THERMOCOMP™ EC008APQ compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| Lucon® CP6052 | LG Chem Ltd. | PC+ABS | Lucon® |
| CERTENE™ PHT-4 | Muehlstein | PP Homopolymer | CERTENE™ |