ACCUTECH™ HP0334T10L
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qB4M0p_ACCUTECH-HP0334T10L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0334T10L is a polypropylene homopolymer (PP Homopoly) product, which contains 10% talc filler. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 36.0 | MPa | ASTM D638 |
| Fracture | 22.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 20 | % | ASTM D638 |
| Flexural Modulus | 1900 | MPa | ASTM D790 |
| Flexural Strength | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 112 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 60.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 10% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 683 HEC FR | RTP Company | ABS | RTP |
| Sylvin 5145-83 White 1358 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Unichem 5514 | Colorite Polymers | PVC, Unspecified | Unichem |
| BESTNYL SE25VI01AWX | Triesa Plastics | Nylon 66 | BESTNYL |
| LNP™ THERMOCOMP™ MF002AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |