MAJ'ECO DP394WT
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qAoeYZ_MAJ-ECO-DP394WT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO DP394WT is a natural fibre reinforced polypropylene compound intended for injection moulding. MAJ'ECO DP394WT has been developed especially for demanding applications in various engineering sectors. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.3 - 1.9 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2950 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 26.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2350 | MPa | ISO 178 |
| Flexural Stress 2 | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 146 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 93.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 150 - 190 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PA66 A309 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| COSMOPLENE® FC9412G | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Random Copolymer | COSMOPLENE® |
| Petlon Prime A2-G30-00-BK | Petlon Polymers Ltd | Nylon 66 | Petlon Prime |
| Therma-Tech™ TT9200-5003 EC Anthracite (EM10018998BJ) | PolyOne Corporation | PPS | Therma-Tech™ |
| Sylvin 2808-80 White 1440 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |