Iupilon® ECF2015R
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qAZTlG_Iupilon-ECF2015R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® ECF2015R is a Polycarbonate (PC) material filled with 15% carbon fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® ECF2015R are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.20 to 0.40 | % | |
| Flow : 3.20 mm | 0.050 to 0.25 | % | |
| Water Absorption (Saturation, 23°C) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 9600 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 146 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.50 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S USZ200 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| Tisoplen® PPH 40 MNF TALC | Tisan | PP Homopolymer | Tisoplen® |
| Tuftec™ H1031 | AKelastomers | SEBS | Tuftec™ |
| Axiall PVC 8266 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Karina BEIGE PVC COMPOUND -E 841-08/184-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |