DESOX™ DSC410I
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qAGUgv_DESOX-DSC410I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESOX™ DSC410I is one of the brands which made by PBT(Poly Butylene Terephthalate) unfilled resin. It provides good electric property and good mechanical strength. Applications: DESOX™ DSC410I is one of the most-used resin requested for electric property and mechanical property such as automotive bezel etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.5 - 2.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 58.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 80 | % | ASTM D638 |
| Flexural Modulus | 2750 | MPa | ASTM D790 |
| Flexural Strength | 93.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 160 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.0 | °C | ASTM D648 |
| Melting Temperature | 222 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 245 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P26M | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Ultraform® S 1320 0021 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Niretan A F50 | Soredi S.p.a. | Nylon 66 | Niretan A |
| Jam PE 02X02 | Jam Petrochemical Company | VLDPE | Jam PE |
| INEOS HDPE T60-1200-119 | INEOS Olefins & Polymers USA | HDPE | INEOS HDPE |