ELITE™ 5230G
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qA94WI_ELITE-5230G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
ELITE™ 5230G Enhanced Polyethylene Resin is produced via INSITE™ Technology from Dow. This resin offers high impact strength and good puncture resistance at moderate stretch levels for irregularly shaped loads. In addition, this resin provides excellent extensibility for higher yields on regular loads.
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.916 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Film Puncture Force 1(20 µm) | 48.9 | N | Internal method |
| Film Puncture Resistance (20 µm) | 27.0 | J/cm³ | Internal method |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 9.07 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 8.39 | MPa | ASTM D882 |
| MD : Break, 20 µm | 46.0 | MPa | ASTM D882 |
| TD : Break, 20 µm | 38.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 540 | % | ASTM D882 |
| TD : Break, 20 µm | 720 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 320 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 310 | g | ASTM D1922 |
| TD : 20 µm | 510 | g | ASTM D1922 |
| Final stretch 2(20.3 µm) | 330 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.3 µm) | 95 | ASTM D2457 | |
| Haze (20.3 µm) | 0.50 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 271 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 模具间隙：20 密尔 (0.50 mm) 熔体温度：520°F (271°C) 气隙：3 英寸 (7.6cm) 脱离速度：600 fpm（183 米/分） |
| Note Message | |
|---|---|
| 1 . | 250% pre-stretch; Test on pallet. |
| 2 . | Test on pallet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ PW2100 resin | SABIC Innovative Plastics Europe | PEI | ULTEM™ |
| Yuyao PBT 3066G20 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| DINAPLEN® PPH1S07 G30 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| Infino LS-3302A | SAMSUNG SDI CO., LTD. | PC | Infino |
| Sylvin 8600-85 Blue 8374 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |