Stanyl® TW272B6
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q9fWtw_Stanyl-TW272B6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TW272B6 is a Polyamide 46 (Nylon 46) material filled with 30% carbon fiber. It is available in Asia Pacific, Europe, or North America. Important attributes of Stanyl® TW272B6 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 24000 | 14500 | MPa | |
| 120°C | 12500 | -- | MPa | |
| 160°C | 11000 | -- | MPa | |
| 180°C | 10500 | -- | MPa | |
| 200°C | 10000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 240 | 160 | MPa | |
| Break, 120°C | 130 | -- | MPa | |
| Break, 160°C | 110 | -- | MPa | |
| Break, 180°C | 100 | -- | MPa | |
| Break, 200°C | 90.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 1.6 | 3.5 | % | |
| Break, 120°C | 3.1 | -- | % | |
| Break, 160°C | 3.1 | -- | % | |
| Break, 180°C | 3.1 | -- | % | |
| Break, 200°C | 3.1 | -- | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ||||
| -30°C | 6.0 | 6.0 | kJ/m² | ISO 179/1e |
| 23°C | 6.0 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 55 | kJ/m² | |
| 23°C | 50 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 3.5E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LP 330 | A. Schulman Europe | ABS | POLYMAN® |
| Staramide PFB42U | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Sylvin 9655-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AKROMID® B3 GF 40 S1 black (3384) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| ICORENE® N4505 | ICO Polymers EMEA, A Division of A. Schulman | PP Random Copolymer | ICORENE® |