KEBAPEAK® PEEK XC1730
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | BARLOG plastics GmbH |
| Trademark: | KEBAPEAK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q96iNd_KEBAPEAK-PEEK-XC1730.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PEEK; 30 % carbon fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.60 | % | |
| Flow | 0.20 | % | |
| Water Absorption (Saturation, 23°C) | 0.040 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 23500 | MPa | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 310 | °C | ISO 75-2/A |
| Melting Temperature 1 | 343 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+5 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (0.800 mm) | V-0 | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-1305/40 NAT | Techmer Engineered Solutions | PPS | TES |
| TRIBIT® LM1503 | Samyang Corporation | PBT | TRIBIT® |
| ACCUTECH™ CP0437G20CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| AKROMID® C3 GF 40 1 black (4658) | AKRO-PLASTIC GmbH | Nylon 66/6 | AKROMID® |
| LUVOCOM® 1105/CF/30/EM | Lehmann & Voss & Co. | PEEK | LUVOCOM® |