ACCUTECH™ HP0334W20L1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q8qglP_ACCUTECH-HP0334W20L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0334W20L1 is a polypropylene homopolymer (PP Homopoly) product containing 20% wollastonite (casio3). It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 34.0 | MPa | ASTM D638 |
| Fracture | 23.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 22 | % | ASTM D638 |
| Flexural Modulus | 2100 | MPa | ASTM D790 |
| Flexural Strength | 48.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 112 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 64.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 20GF GWT 960 | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| BMC 620X | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| ASI POLYETHYLENE EVA | A. Schulman Inc. | PE, Unspecified | ASI POLYETHYLENE |
| INEOS HDPE K54-05 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| Iupilon® EFR2151H | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |