Impet® 2700 GV1/20
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Impet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q8dO31_Impet-2700-GV1-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyethylene terephthalate, 20 % glass fibre reinforced, high flowability, excellent gloss, high modulus |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.90 | % | ISO 294-4 |
| Flow direction | 0.30 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 123 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 133 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 8100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 173 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.6 | kJ/m² | ISO 179/1eA |
| 23°C | 6.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 20 | kJ/m² | ISO 179/1eU |
| 23°C | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 7.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 248 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 233 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 80.0 | °C | ISO 75-2/C |
| Glass Transition Temperature 1 | 80.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| Melting Temperature 2 | 250 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 9.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 31 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.60 | IEC 60250 | |
| 1 MHz | 4.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.0E-3 | IEC 60250 | |
| 1 MHz | 0.019 | IEC 60250 | |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Oxygen Index | 24 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 135 - 145 | °C | |
| Injection Pressure | 60.0 - 90.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 50.0 | MPa | |
| Back Pressure | 1.00 - 2.00 | MPa | |
| Screw Speed | 50 - 80 | rpm |
| Injection instructions |
|---|
| Feed Temperature: 40 to 60°CZone 4 Temperature: 280 to 290°CManifold Temperature: 270 to 290°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 128 LF | RTP Company | PP Homopolymer | RTP |
| Sasol Polymers PE LT033 (Extrusion/Blow molding) | Sasol Polymers | LDPE | Sasol Polymers PE |
| ENSOFT SU-141-20A | ENPLAST, a Ravago Group Company | TPE | ENSOFT |
| INNOMID® CS 6-9830 HD | Inno-Comp Ltd. | Nylon 6 Alloy | INNOMID® |
| Sylvin 8215-85UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |