Hylex® P1303L1 HB
| Category: | PC , Polycarbonate |
| Manufacturer: | Entec Polymers |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q7ttOZ_HylexP1303L1HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYCARBONATE, UV STABILIZED, BRANCHED FOR EXTRUSION & BLOW MOLDING |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 61.0 | MPa | ASTM D638 |
| Fracture, 23°C | 58.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 6.0 | % | ASTM D638 |
| Fracture, 23°C | 96 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2300 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 97.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 810 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 141 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.8 mm | HB | UL 94 | |
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDINYL PMD 20104 | ADDIPLAST | Nylon 66 | ADDINYL |
| KRATON® D1152 E | Kraton Polymers LLC | SBS | KRATON® |
| Lupoy® 1302UV-08 | LG Chem Ltd. | PC | Lupoy® |
| Horda E8406 | Horda Cable Compounds | EVA | Horda |
| Hostacom EKC 330N NA 4PK SOUL | LyondellBasell Industries | TPO (POE) | Hostacom |