LNP™ LUBRICOMP™ NXCY620 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q7lGOn_LNP-LUBRICOMP-NXCY620-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* NXCY620 is a compound based on Cycoloy* XCY620 containing Silicone. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound NXCY620 Product reorder name: NXCY620 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.14 | g/cm³ | |
| -- | 1.13 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.80 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption (24 hr, 50% RH) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2190 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 51.0 | MPa | ASTM D638 |
| Yield | 49.0 | MPa | ISO 527-2/5 |
| Break 3 | 40.0 | MPa | ASTM D638 |
| Break | 42.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.7 | % | ASTM D638 |
| Yield | 4.9 | % | ISO 527-2/50 |
| Break 5 | 31 | % | ASTM D638 |
| Break | 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2220 | MPa | ASTM D790 |
| -- 7 | 2120 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 77.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 79.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.23 | ||
| vs. Itself - Static | 0.18 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 7.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 1250 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 39 | kJ/m² | |
| 23°C | 51 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 650 | J/m | ASTM D256 |
| -40°C 9 | 28 | kJ/m² | ISO 180/1A |
| 23°C 10 | 48 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 125 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 108 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 110 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 105 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 250 to 290 | °C | |
| Nozzle Temperature | 240 to 280 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 1200H-15 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Sinkral® F 332 | Versalis S.p.A. | ABS | Sinkral® |
| Evermore PUR UP-6015NR | Evermore Chemical Industry Co., Ltd. | PUR-Ester | Evermore PUR |
| KEBAFORM® C 90 M | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Sylvin 4200-85AM Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |