Homopolymer Polypropylene, 20% Glass Reinforced, Natural Color, 10 Melt Flow |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
RoHS Compliance |
|
Appearance |
|
Forms |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Yield, 23°C) | 81.4 | MPa | ASTM D638 |
Tensile Elongation | ASTM D638 | ||
Yield, 23°C | 3.0 | % | |
Break, 23°C | 4.0 | % | |
Flexural Modulus - Tangent (23°C) | 3520 | MPa | ASTM D790 |
Flexural Strength (23°C) | 93.1 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C, 3.18 mm) | 85 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, Unannealed | 149 | °C | |
1.8 MPa, Unannealed | 132 | °C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
ESTAPROP H0560 GFC/NT | Cossa Polimeri S.r.l. | PP Homopolymer | ESTAPROP |
Exxtral™ Performance Polyolefin CNU011 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
Fluon® PTFE PB2015 | Asahi Glass Co., Ltd. | PTFE | Fluon® |
OmniLon™ PA6/6 S12 FD | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
ALTECH® PA66 ECO 1000/617 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |