SABIC® LDPE 2201H1 Datasheet,LDPE,Saudi Basic Industries Corporation (SABIC)-SHANGHAI SUSHENG

Message
SABIC® LDPE 2201H1 is a grade with a low level of anti block and a medium level of slip agent (E=erucamide). Blown Film: The grade has a very good draw down ability. Films based on 2201H1 combine toughness with high tear strength, good optical properties and low CoF. Cast Film: Films made from this grade typically show good optical properties, processability and draw down. Application SABIC® LDPE 2201H1 is typically developed for lamination films, high quality carrier bags and high quality packaging films. This product is not intended for and must not be used in any pharmaceutical/medical applications.

General Information
Additive	Low caking resistance (210 ppm) Erucamide Lubricating Additive (450 ppm)
Features	Low caking resistance Low density Low friction coefficient Optical Workability, good Good stripping Good tear strength Good toughness Moderate smoothness
Uses	Blown Film Packaging Laminate Bags cast film
Processing Method	Blow film cast film

Physical	Nominal Value	Unit	Test Method
Density	0.922	g/cm³	ISO 1183/A
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.85	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (Blown Film)	0.15		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested
-- ¹	25	µm
-- ²	50	µm
Tensile Modulus			ISO 527-3
MD : 25 µm, cast film	140	MPa	ISO 527-3
TD : 25 µm, cast film	140	MPa	ISO 527-3
MD : 50 µm, blown film	170	MPa	ISO 527-3
TD : 50 µm, blown film	170	MPa	ISO 527-3
Tensile Stress			ISO 527-3
MD : Yield, 25 µm, cast film	9.00	MPa	ISO 527-3
TD : Yield, 25 µm, cast film	8.00	MPa	ISO 527-3
MD : Yield, 50 µm, blown film	11.0	MPa	ISO 527-3
TD : Yield, 50 µm, blown film	11.0	MPa	ISO 527-3
MD : Fracture, 25 µm, cast film	24.0	MPa	ISO 527-3
TD : Fracture, 25 µm, cast film	17.0	MPa	ISO 527-3
MD : Broken, 50 µm, blown film	25.0	MPa	ISO 527-3
TD : Broken, 50 µm, blown film	20.0	MPa	ISO 527-3
Tensile Elongation			ISO 527-3
MD : Fracture, 25 µm, cast film	260	%	ISO 527-3
TD : Fracture, 25 µm, cast film	580	%	ISO 527-3
MD : Broken, 50 µm, blown film	> 200	%	ISO 527-3
TD : Broken, 50 µm, blown film	> 500	%	ISO 527-3

Impact	Nominal Value	Unit	Test Method
Impact Strength			ASTM D4272
Blown Film : 50.0 µm	250	J/cm	ASTM D4272
Cast Film : 25.0 µm	220	J/cm	ASTM D4272

Additional Information	Nominal Value	Unit	Test Method
Blocking (50.0 µm) ³	50	g	Internal method
Re-blocking (50.0 µm) ⁴		g	Internal method
Tear Strength ⁵			ISO 6383-2
MD : 50.0 µm	45.0	kN/m	ISO 6383-2
TD : 50.0 µm	45.0	kN/m	ISO 6383-2

Optical	Nominal Value	Unit	Test Method
Gloss			ASTM D2457
45, 50.0 µm, blown film	65		ASTM D2457
45, 25.0 µm, cast film	73		ASTM D2457
Haze			ASTM D1003A
50.0 µm, blown film	6.0	%	ASTM D1003A
25.0 µm, cast film	4.9	%	ASTM D1003A

Additional Information	Nominal Value	Unit	Test Method
Cast FilmThe optical and film properties are determined on 25 µm cast film. Die gap 1.0 mm.Blown FilmFilm properties have been measured at film of 50 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm.

Category:	LDPE , Low Density Polyethylene
Manufacturer:	Saudi Basic Industries Corporation (SABIC)
Trademark:	SABIC® LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	q7DbAG_SABIC-LDPE-2201H1.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RheTech Polypropylene G13P100-01UV	RheTech, Inc.	PP, Unspecified	RheTech Polypropylene
SLOVALEN® PH 59 T 40 LW 031	Plastcom	PP, Unspecified	SLOVALEN®
Staramide A24G6K	Eurostar Engineering Plastics	Nylon 66	Staramide
WanBlend® WHT-8185M	Wanhua Chemical Group Co., Ltd.	TPU-Polyether	WanBlend®
ExxonMobil™ EnBA EN 33331	ExxonMobil Chemical	EnBA	ExxonMobil™ EnBA