Jamplast high gloss resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. Jamplast ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes. Jamplast ABS resins are designed to offer a wide range of impact strengths and melt flow rates to meet the needs of the durables injection molding markets. This product offers typical Izod impact strength values from 4 to 7.5 ft-lb/in and melt flow rates ranging from 2.5 to 7.0 g/10 min. The gloss values are typically greater than 95% on the 60° Gardner scale for the highest gloss resins and greater than 90% for those products having a broader range of gloss. Jamplast ABS resin offers a broader range of gloss while maintaining medium impact strength with a medium melt flow rate. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2240 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 44.8 | MPa | |
| Break | 31.0 | MPa | |
| Tensile Elongation 3(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 4 | 2550 | MPa | ASTM D790 |
| Flexural Strength 5 | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6 | ASTM D256 | ||
| -18°C, 3.18 mm | 130 | J/m | |
| 23°C, 3.18 mm | 320 | J/m | |
| Instrumented Dart Impact 7 | ASTM D3763 | ||
| -18°C, 3.18 mm, Peak Energy | 26.0 | J | |
| -18°C, 3.18 mm, Total Energy | 31.6 | J | |
| 23°C, 3.18 mm, Peak Energy | 33.9 | J | |
| 23°C, 3.18 mm, Total Energy | 55.4 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 92.2 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 76.7 | °C | |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| CLTE - Flow | 7.9E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 90 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 218 to 274 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 3.45 | MPa | |
| Clamp Tonnage | 2.8 to 6.9 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 3.5:1.0 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 1.3 mm/min |
| 5 . | Type I, 1.3 mm/min |
| 6 . | 0.25 mm Notch Depth |
| 7 . | 3.39 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Visico™ LE4423/Ambicat™ LE4476 | Borealis AG | XLPE | Visico™ |
| Xuchuan XCW-H8928 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Hifax TRC 280X NA Black | LyondellBasell Industries | PP Copolymer | Hifax |
| Plaslube® NY-6/MS/M | Techmer Engineered Solutions | Nylon 12 | Plaslube® |
| Sylvin 4299-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |