Zytel庐 HTN FR52G30BL BK337
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q4xDVa_Zytel-HTN-FR52G30BL-BK337.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Flame Retardant, PPA, High Performance Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.62 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11800 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 160 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | -- | % | ISO 527-2 |
| Flexural Modulus | 10000 | -- | MPa | ISO 178 |
| Flexural Stress | 240 | 210 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 35 | kJ/m² | |
| 23°C | 50 | 35 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 282 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 310 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 2.0E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 1.0E-4 | -- | cm/cm/°C | |
| Transverse | 6.3E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 5.7E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.50 | -- | ||
| 1 MHz | 3.30 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.0E-3 | -- | ||
| 1 MHz | 0.014 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 5VA | -- |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 35.0 | -- | µgC/g | VDA 277 |
| Odor | 3 | -- | VDA 270 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® A3 GF 30 5 black (2180) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| DURACON® CH-15 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| HANWHA KL-701 | Hanwha Chemical | PVC, Unspecified | HANWHA |
| Petrothene® NA860 | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 5145-88UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |