Fortron® 4184L6
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q4sGsD_Fortron-4184L6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron 4184L6 is an easier flow version of Fortron 4184L4. It offers similar characteristics to the 4184L4. This grade is especially used for thin walled parts requiring long flow lengths, stiffness and dimensional control. Applications made of this grade are typically electronic components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.556 | cm³/g | ASTM D792 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat Capacity of Melt | 1500 | J/kg/°C | Internal method |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | |||
| Flow | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow | 0.40 - 0.60 | % | ASTM D955 |
| Vertical flow direction | 0.40 - 0.70 | % | ISO 294-4 |
| Flow direction | 0.30 - 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class m | 100 | ASTM D785 | |
| M scale | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16600 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 165 | MPa | ASTM D638 |
| Fracture | 165 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.5 | % | ASTM D638 |
| Fracture | 1.4 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 16200 | MPa | ISO 178 |
| Flexural Stress 1 | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 29 | kJ/m² | ISO 179/1eU |
| 23°C | 29 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 27 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, annealed | 280 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 265 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 270 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 215 | °C | ISO 75-2/C |
| Glass Transition Temperature 2 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 27 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 kHz | 3.80 | ASTM D150 | |
| 1 MHz | 3.80 | ASTM D150 | |
| 1 MHz | 4.70 | IEC 60250 | |
| Dissipation Factor | |||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 8.0E-4 | ASTM D150 | |
| 1 MHz | 2.0E-3 | IEC 60250 | |
| Arc Resistance | 156 | sec | ASTM D495 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | 10°C/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4005 A | RTP Company | PPA | RTP |
| RTP 1000 MS 2 | RTP Company | PBT | RTP |
| Argothane® 19424 | Argotec LLC | TPU, Unspecified | Argothane® |
| OPTICITE™ SQZ White | The Dow Chemical Company | Polyolefin, Unspecified | OPTICITE™ |
| Sylvin 8600-75 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |