Starflam PK0069
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starflam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q4GYxp_Starflam-PK0069.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starflam PK0069 is a Flame Retardant Mineral Filled Polyamide 6 Injection Molding Resin (also known Starflam PA6 30E6 U2 Z88) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.66 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.70 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 63.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7400 | MPa | ISO 178 |
| Flexural Stress | 101 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 2.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 15 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 193 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 130 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A ESL128 | Radici Plastics | Nylon 66 | Radilon® |
| Mirathane™ E695 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| ALCOM® PA6 900/1 GF30 WT1165-10LB | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Fainplast PVC CKL 8318/2 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Latilub 66-10T K/10 | LATI S.p.A. | Nylon 66 | Latilub |