Stat-Tech™ AS-1000 AS
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q49d4g_Stat-Tech-AS-1000-AS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low to high levels of conductivity depending upon application requirements. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 8.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 to 0.60 | % | |
| Across Flow | 0.40 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1940 | MPa | ASTM D638 |
| Tensile Strength (Break) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 20700 | MPa | ASTM D790 |
| Flexural Strength | 59.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 210 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 87.0 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 74.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 to 1.0E+12 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+11 to 1.0E+12 | ohms·cm | ASTM D257 |
| Static Decay | |||
| (Mil-B-81705C), 12% RH, 5000 kV to 50 kV | 0.3 | sec | |
| (Mil-B-81705C), 50% RH, 5000 kV to 50 kV | 0.1 | sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 227 to 238 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GF 25 FRG 5 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Styropor® P 426 C | BASF Corporation | PS (EPS) | Styropor® |
| Synthos EPS® 0308F/PL | Synthos S.A. | PS (EPS) | Synthos EPS® |
| ALCOM® PC 740/4 GY1281-04LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| LNP™ THERMOCOMP™ DC0049XF compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |