Jampilen HP483R
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Jam Polypropylene Company |
| Trademark: | Jampilen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q3uckB_Jampilen-HP483R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jampilen HP483R is a homopolymer for injection molding with antistatic and slip agent additivation that exhibits good stiffness combined with good flowability. The main applications of Jampilen HP483R are caps, closures, furniture and TWIM. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 68.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 9.0 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 151 | °C | ISO 306/A50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermec™ 4150RMC65 | Technical Polymers, LLC | PPS | Thermec™ |
| Nycast 6PA | Cast Nylons Ltd. | Nylon 6 | Nycast |
| APEX® 04-A769R-70NT | Teknor Apex Company | PVC, Flexible | APEX® |
| KEP® 2380 | Kumho Polychem Co., Ltd. | EPDM | KEP® |
| InnoPlus LD2420K | PTT Global Chemical Public Company Limited | LDPE | InnoPlus |