Plenco 05350 (Compression)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q3U4F6_Plenco-05350-Compression-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 05350 is a mineral and graphite filled phenolic molding compound, developed for seal applications. PLENCO 05350 offers excellent dimensional stability, lubricity, and low abrasion properties. 05350 is available in gray. 05350 is not recommended for electrical insulating applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.74 | g/cm³ | ASTM D792 |
| Apparent Density | 0.92 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.24 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14800 | MPa | ASTM D638 |
| Tensile Strength | 31.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.30 | % | ASTM D638 |
| Flexural Modulus | 13200 | MPa | ASTM D790 |
| Flexural Strength | 63.1 | MPa | ASTM D790 |
| Compressive Strength | 142 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 14.5 | J/m | ASTM D256 |
| Notched Izod Impact | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 193 | °C | ASTM D648 |
| Continuous Use Temperature | 249 | °C | ASTM D794 |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity (100°C) | 1.9 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 41 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity, ASTM C177 was tested according to the ASTM E1461 standard.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.07%Drop Ball Impact, PLENCO Method: 35 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 0.50 | hr | |
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Mold Close Time: 3-8 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 A X 117575 A | RTP Company | Nylon 6 | RTP |
| Braskem PP TI4700P2 | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| Lastilac MR MDT05-01 | LATI S.p.A. | ABS | Lastilac |
| K-vinyl KK-I-A88 | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| Sylvin 9604A-80 Clear 8159 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |