SCHULAMID® 66 GF 30 HE LW
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q37CXM_SCHULAMID-66-GF-30-HE-LW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced and heat stabilized polyamide 66-compound, electrical neutral, transparent for laser light of laser welding processes |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 160 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9800 | 5800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 180 | 96.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.5 | 8.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 8200 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 270 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 4.5 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 12 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | -- | kJ/m² | |
| 23°C | 85 | 78 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | > 250 | -- | °C | ISO 306/A50, ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 15 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 650 | -- | °C | |
| 3.00 mm | 675 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 675 | -- | °C | |
| 3.00 mm | 700 | -- | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene F37-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Fainplast PVC PH 75/G | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Ferro PP LPP60BC67NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Axiall PVC 7434 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Moplen HP552R | LyondellBasell Industries | PP Homopolymer | Moplen |