Ferro PP TPP40AE62BK
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q1eT85_Ferro-PP-TPP40AE62BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
25% minimum post consumer recycle (P.C.R.) Meets/Exceeds Ford Engineering Specification WSL-M4D910-A. Primary end use is for fan shrouds. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.3 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 30.5 | MPa | ISO 527-2 |
| Flexural Modulus | 3400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -40°C | 1.6 | kJ/m² | ISO 180 |
| 23°C | 2.3 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 89.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tensile/Izod Change, ISO 188, 1000 hours, 140°C: +3%/+8% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayblend® W85 XF | Covestro - Polycarbonates | ASA+PC | Bayblend® |
| Arnite® T06 200 SNF | DSM Engineering Plastics | PBT | Arnite® |
| Geon™ Vinyl Flexible XV3884 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hyundai EP Adhesives LE149V/1002 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP Adhesives |
| INEOS PP N05U-00 | INEOS Olefins & Polymers USA | PP Impact Copolymer | INEOS PP |