Sindustris PP M1426
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q0ghSZ_Sindustris-PP-M1426.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PP M1426 is a Polypropylene material. It is available in Asia Pacific. Typical applications include:
|
| General Information | |
|---|---|
| Uses |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 27.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 200 | % | ASTM D638 |
| Flexural Modulus | 177 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 130 | °C | ASTM D648 |
| Vicat Softening Temperature | 155 | °C | ASTM D1525 3 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9960 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sinvicomp SIM5520 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TOTAL Polystyrene Impact 3630 | TOTAL Refining & Chemicals | PS (MIPS) | TOTAL Polystyrene |
| INSULCAST® 333/INSULCURE 20 | ITW Polymers Coatings North America | Epoxy | INSULCAST® |
| Badaflex® TPU 90A 8030 CF17 | Bada AG | TPU, Unspecified | Badaflex® |