Order Products : sales@su-jiao.com
KOPPS® S21A65
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPPS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q0BO5B_KOPPSS21A65.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPPS®S21A65 is a polyphenylene sulfide (PPS) product, which contains a 65% filler. It is available in North America, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.95 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.18 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ISO 294-4 |
| Flow | 0.23 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.020 | % | ISO 62 |
| Balanced, 23°C, 60% RH | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 122 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 98.1 | MPa | ASTM D638 |
| 23°C | 125 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.0 | % | ASTM D638 |
| Fracture, 23°C | 1.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 18600 | MPa | ASTM D790 |
| 23°C | 16000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 196 | MPa | ASTM D790 |
| 23°C | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 285 | °C | ISO 11357-3, ASTM D3418 |
| CLTE - Flow | 2.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.00 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Comparative Tracking Index | 230 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 120 - 130 | °C | |
| Drying Time - Desiccant Dryer | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 300 - 320 | °C | |
| Mold Temperature | 120 - 140 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9A22120 | 4Plas | Nylon 66 | 4MID® |
| Asiga® PlasGRAY | Asiga | Unspecified | Asiga® |
| LG ABS XG568 | LG Chem Ltd. | ABS | LG ABS |
| omay® SE11 | Suzhou OMAY Optical Materials Co., Ltd | Film, PC | omay® |
| Pinnacle PP 5120H | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |