BCC Resins DP-11-88
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BCC Products Inc. |
| Trademark: | BCC Resins |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q05cUA_BCC-Resins-DP-11-88.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DP-11-88 is a medium viscosity quick setting easy to use urethane adhesive. This system was specifically designed to bond together the MB2001/MB3000 Model/Tooling Board to create desired dimensions in length, width, and height. DP-11-88 offers a working life of 10 to 12 minutes in 1/4 pound mass, and 20 + minutes in a 1/16 inch film. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.778 | g/cm³ | ASTM D792 |
| -- | 0.775 | g/cm³ | ASTM D1505 |
| Specific Volume | 1.27 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 12.0 to 14.0 | min | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Life 1(24°C) | 10.0 to 12.0 | min |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.10 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 14.9 | MPa | ASTM D638 |
| Flexural Modulus | 1160 | MPa | ASTM D790 |
| Flexural Strength | 23.4 | MPa | ASTM D790 |
| Compressive Strength | 19.1 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 62.8 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Thermoset Mix Viscosity | ASTM D2393 | ||
| -- 2 | 3750 | cP | |
| -- 3 | 4500 | cP | |
| -- 4 | 3000 | cP | |
| Demold Time 5(24°C) | 480 to 720 | min |
| Note Message | |
|---|---|
| 1 . | 1/2 lb mass |
| 2 . | Mixed |
| 3 . | Part B |
| 4 . | Part A |
| 5 . | Adhesive |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIMONA® PVC-CAW | SIMONA AMERICA, Inc. | PVC, Rigid | SIMONA® |
| Talcoprene® C340TC NATURALE | SO.F.TER. SPA | PP Copolymer | Talcoprene® |
| Vistalon™ 7001 | ExxonMobil Chemical | EPDM | Vistalon™ |
| Karina IVORY PVC COMPOUND 750-35/1-B-AC-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF00AH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |