Generic Polyester, TP
| Category: | Polyester, TP , Thermoplastic Polyester |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pzX9Q6_Generic-Polyester-TP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Polyester, TP This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 - 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.29 - 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.066 - 0.16 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 103 - 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 46.0 - 58.9 | MPa | ASTM D638 |
| Yield, 23°C | 46.2 - 47.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 29.0 - 53.9 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 4.0 - 5.1 | % | ASTM D638 |
| Fracture, 23°C | 39 - 500 | % | ASTM D638 |
| Fracture, 23°C | 190 - 210 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1520 - 2340 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 65.0 - 73.8 | MPa | ASTM D790 |
| Yield, 23°C | 67.0 - 69.0 | MPa | ASTM D790 |
| Coefficient of Friction | 0.37 - 0.51 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 29 - 52 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 85.9 - 101 | MPa | ASTM D882 |
| TD : Yield | 85.5 - 103 | MPa | ASTM D882 |
| MD : Fracture | 156 - 193 | MPa | ASTM D882 |
| TD : Fracture | 182 - 230 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 140 - 200 | % | ASTM D882 |
| TD : Fracture | 95 - 110 | % | ASTM D882 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 - 380 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C) | 31.7 - 46.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 67.0 - 73.2 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 60.6 - 70.5 | °C | ASTM D648 |
| Vicat Softening Temperature | 79.0 - 86.5 | °C | ASTM D1525 |
| Melting Temperature | 255 - 260 | °C | |
| CLTE - Flow | 1.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (23°C) | 2.34 - 3.30 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 88.6 - 92.0 | % | ASTM D1003 |
| Haze | 0.20 - 2.6 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 69.8 - 80.9 | °C | |
| Drying Time | 3.0 - 4.1 | hr | |
| Processing (Melt) Temp | 255 - 270 | °C | |
| Mold Temperature | 22.5 - 22.6 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Polyester, TPThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 CF 10 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Epoxies, Ect. 10-2080 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |
| IROGRAN® A 95 E 4813 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| ALCOM® PC 740/4 BL 1355-06LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| STYRON™ 686E | Trinseo | PS (GPPS) | STYRON™ |